6AL-4V Eli Titanium
Alternate Names: Grade 23 Titanium, 6-4 Eli Titanium
Description: 6AL-4V Eli is an alloyed Grade of Titanium. It is strengthened by the inclusion of roughly 6% Aluminum and 4% Vanadium. Titanium 6AL-4V Eli (Extra-Low Interstitial) is considered a higher purity than 6AL-4V Grade 5 due to its lower inclusions of Iron, and the interstitial elements, Carbon and Oxygen. 6AL-4V Eli typically comes in the annealed condition, but can be found in beta annealed condition as well. 6AL-4V Eli Grade 23 shows high strength and toughness, as well as good corrosion resistance. It is found in aerospace applications where fracture toughness and fatigue strength are important. As a biocompatible Grade of Titanium, it is also known for its applications in medical and dental industries.
Machinability: The American Iron and Steel Institute (AISI) determined a rating system of machinability of different materials. 160 Brinell B1112 steel was arbitrarily assigned a machinability rating of 100%. Using this as a comparable standard, ratings less than 100% are more challenging to machine, and ratings more than 100% are easier to machine. Titanium 6AL-4V Eli is rated at 22% of B1112. Low cutting speeds, heavy feed rates, sharp tools, and ample cutting fluid are prescribed.
6AL-4V Eli Titanium is available in the following Specifications:
|AMS 4907||ASTM B265 (Grade 23)||AMS-T-9046 (AB-2 6AL-4V ELI)|
|AMS 4930||ASTM B348 (Grade 23)||AMS-T-9047 (6AL-4V ELI)|
|AMS 6932||ASTM F136||MIL-T-9046 (AB-2 6AL-4V ELI)|
|MIL-T-9047 (6AL-4V ELI)|
Don’t see what you want? Call us at 888-772-8984 for a Quote on 6AL-4V Eli Grade 23 Titanium, or Email us at Sales@performancetitanium.com!
The use of this information is strictly voluntary and should be used as a guideline only. This data contains generalizations and is in no way a substitute for your own research. This information is not intended as a warranty or fitness of any application. Should you require further information about Titanium 6AL-4V Eli Grade 23, please contact us and we will gladly refer you to additional sources.